TECHNICAL DATA SHEET
Titan 7620 is a single component anaerobic retaining and locking adhesive, which
develops high strength and high heat resistance. Titan 7620 is used to bond cylindrical
parts: it may be applied to retain pulleys, gears, rotors and shafts; as well as to secure
bushings, bearings and housing plugs. Titan 7620 will also augment shrink and press fit
assemblies in high-heat and high-friction environments.
Physical Properties - Monomer (Uncured)
Base Compound
Appearance
Viscosity
Specifications and Approvals
Methacrylate Ester
Green Liquid
8500 +/- 3500 cps
None
Hot Strength (%RT strength, tested at temperature)
(Brookfield Spindle 3 @ 20 rpm, RVT, 25°C)
Gap Fill
Specific Gravity
Flash Point
Shelf Life
Storage Condition
RoHS-Compliant
120%
0.16"
1.1
>200°F / 93°C
12 months unopened
20°C / 68°F
yes
100%
80%
60%
Physical Properties - Polymer (Cured)
Appearance
Locking Strength
Service Temp Range
Full Cure Time
Pin/Collar Strength
Green Solid
High
-65 to 400 °F
24 hours
2700
psi
18.62
N/mm2
40%
20%
( -54
to
204 °C)
0%
-40°C
inch-pounds
Newton meters
Breakaway Torque
150.0
to
250.0
16.95
to
28.25
Prevailing Torque
200.0
to
no limit
22.60
to
no limit
Setting Time / Full Cure Time*
15
15
20
20
minutes
minutes
minutes
minutes
/
/
/
/
24
24
24
24
200%
175%
150%
125%
100%
75%
50%
25%
0%
100°C
130°C
60C
80C
100C
Hours
0
hrs
hrs
hrs
hrs
1000
2000
3000
Solvent Resistance
Solvent
Alcohol
Ester (aromatic)
*68°F / 20°C, 65% RH
Example
Resistance
Ethanol, Methanol
+++
Ethylacetate
–––
Ketone (aromatic) Acetone, Benzophenone
Steel
0
5
10
15
Set Time in Min
20
25
++–
Benzyl, Toluol, Xylol
++–
Halogenated
hydrocarbons
Brass
Petrol, Heptanes, Hexane
Aromatic
hydrocarbons
Zinc-Plated
–––
Aliphatic
hydrocarbon
(alkanes)
Stainless
Steel
Cyberbond LLC
888.525.6122
50°C
Heat Aging (aged at temp indicated and tested @ 22°C)
Performance of Cured Adhesive
Steel
Brass
Zinc-Plated
Stainless Steel
0°C
Methylenchloride,
Chloroform,
Chlorobenzol
–––
Weak aqueous
acid
Nitrite, muriatic acid,
sulphuric acid,
phosphoric acid
+ + + (– – – if
concentrated)
Weak aqueous
base
sodium hydroxide
solution, caustic potash
+ + + (– – – if
concentrated)