TECHNICAL DATA SHEET
Apollo 2003 is a single component low viscosity cyanoacrylate adhesive, suitable for
general-purpose applications on metals rubbers and plastics. Apollo 2003 is approved to
ISO 10993-5 for biocompatibility, making it suitable for use in medical device applications.
Physical Properties - Monomer (Uncured)
Specifications and Approvals
Base Compound
Ethyl
Appearance
Clear
10993-5
10993-5
Mil-A-46050C, Type II Class I, A-A-3097, Type II Class 1
Viscosity
50 +/- 20
Specific Gravity
1.06 g/cc
Flash Point
85°C/ 185°F
Shelf Life
12 mo
Storage Condition
20°C/ 68°F
RoHS-Compliant
yes
80%
Physical Properties - Polymer (Cured)
60%
Full Cure Time
Hot Strength (%RT strength, tested at temperature)
120%
100%
24 hours
Appearance
cPs
Clear
Service Temp Range
-55
to
40%
95 °C
( -67
to
20%
203 °F)
0%
-40°C
0°C
50°C
100°C
130°C
Time Until Full Cure (% of RT strength)
Setting Time
10 to 50
5 to 7
4 to 10
Steel
ABS
EPDM
seconds
seconds
seconds
120%
100%
80%
Performance of Cured Adhesive
N/mm²
Substrate
60%
PSI
2520
to
2920
40%
15.2
630
to
2200
15.8
1830
2290
20%
to
to
22.9
2590
to
3320
14.2
to
23.4
2065
to
3400
15.1
to
16.4
2185
to
2375
17.4
to
20.1
Rubber*
4.3
to
AL
12.6
to
PC**
17.9
PVC**
ABS**
Steel
0%
Cure
5 min
10 min
30 min
60 min
240 min
Heat Aging (aged at temp indicated and tested @ 22°C)
*Rubber figures given are typical. Your results may vary by specific rubber type.
**Tested to ASTM 4501
***n/r = not recommended
100%
Performance Range, by Substrate
0.0
5.0
10.0
15.0
N/mm2
20.0
25.0
30.0
80%
35.0
60C
40.0
60%
80C
PVC
40%
100C
PC
20%
ABS
AL
0%
Rubber
(typical)
0
1000
2000
Hours
Steel
0
1000
2000
3000
PSI
4000
5000
6000
Cyberbond LLC...