| Technical Data Sheet Titan 7490 | | |||||||||
Product Description Titan 7490 is a single component, very low viscosity anaerobic threadlocking adhesive, which develops medium to high strength. The product cures between close fitting metal parts where there is an absence of air. Titan 7490 has extra fluorescent tracer dye for ease of detection. Typical Applications Prevents loosening and leaking of threaded fasteners. Suitable for preassembled components. Low viscosity and capillary action allows adhesive to wick into a threaded assembly. Can also be used to fill porosity in welds and castings. Physical Properties | Curing Performance The gap of the bond line will affect set speed. Smaller gaps tend to increase the speed. Activators can be applied to improve set speed but may also impair overall adhesive performance. | ||||||||||
Polymer (Cured) Locking Strength Appearance Service Temperature Range Full Cure Time Sheer Strength (steel nuts and bolts) | High Green Solid -60°F to 300°F 24 Hours 2000 psi | ||||||||||
Performance of Cured Materials Bond strength after 24 hours at 20° to 25°C on steel nuts and bolts. | |||||||||||
Monomer (Liquid) Base Compound Appearance Viscosity (cP @ 68°F) Specific Gravity (g/cc) Gap Fill Corrosivity Flash Point (TCC) Toxicity Shelf Life @40°F | Dimethacrylate Ester Blue liquid 10 cP 1.07 .003" None >200°F Low 1 year unopened | ||||||||||
| |||||||||||
Temperature Resistance % Retained strength when tested at temperature | |||||||||||
Military Specifications Mil-S-46163A Type III, Grade R Curing Properties The rate of cure will depend on environmental conditions and the substrates used. Setting Time (68*F, 65% R.H.) | 100.00 | Strength at Temperature | |||||||||
| |||||||||||
TS m c '5 | 80.00 60.00 | ||||||||||
40.00 5s20.00 0.00 | |||||||||||
0 60 80 100 120 150 Temperature , C | |||||||||||
Substrate Steel Brass Zn Dichromate Stainless Steel | Set time/Full Cure 10 min/24 hrs 20 min/24 hrs 55 min/24 hrs 60 min/24 hrs | ||||||||||
Page 1 of 2 |