636 S-2 Glass® Yarn
High-Strength Solutions for Your Toughest
Reinforcement Challenges
AGY’s S-2 Glass® high-strength bers
are specically designed to meet
your most demanding performance
processing and cost requirements.
AGY’s global network of people and
facilities are ready to help you
develop innovative solutions to your
most difcult reinforcement
challenges.
Product Application
636 S-2 Glass yarn is designed to be
used in transportation, construction
and recreation applications such as:
• Aircraft cargo liners
• High temperature insulation
• High temperature ltration
• Surfboards
Aircraft Cargo Liner
Product Solutions
S-2 Glass bers offer a unique
combination of properties: strength,
impact resistance, stiffness, radar
transparency and temperature and
fatigue resistance. Compared with
other reinforcing materials, S-2 Glass
bers weigh less than conventional
glass ber and deliver better cost
performance than aramid and carbon
bers. In addition, these yarns meet
the requirements of MIL-Y-114OH
specications.
Product Description
636 S-2 Glass direct sized yarns
consist of numerous laments of
varying diamters, twisted to form
yarns. The material’s starch-oil sizing,
which protects the glass laments
from abrasion during processing, is
typically removed after processing
and the fabric is treated with a resin
compatible nish.
S-2 Glass Fiber Yarn
Features
Benets
S-2 Glass ber offers signicantly
more strength than conventional glass
ber: 85% more tensile strength in
resin impregnated strands
Consistent high performance for
reliable and durable nished parts
Better ber toughness, modulus of
resilience and impact deformation
than conventional glass ber
Improved impact capabilities to
nished parts and higher
composites durability and
damaged tolerance
Softening point: 1056°C (1932°F)
Annealing point: 816°C (1500°F)
Strain point: 766°C (1410°F)
Greater ber tensile strength and
stability at elevated temperatures
in thermoset and thermoplastic
applications
Enhanced stiffness
Delivers 25% more linear-elastic
stiffness than conventional glass
ber
Excellent tolerance to damage
accumulation
The ability of composite parts to
withstand high levels of tension
and exural fatigue without
catastrophic failure
Resin Compatibility
• Starch-oil sized for weaving and
processing
S-2 Glass bers deliver 20% reduction
Radar transparency
in dielectric constant over E-Glass bers
Long shelf life, good machinability and
excellent durability
Consistent performance and
reliability
Processes
• Weaving • Braiding • Plying
S-2 Glass ber is an organic material
Fire resistant
S-2 Glass ber’s pristine white color
provides consistent cosmetics
Consistent appearance
"