New DELO-ML0 pages
NEW DELO-ML
High-strength, fast and exible
Your benefits at a glance:
Extensive consultation on your specic
bonding task
Specic adhesive selection
Sample bondings and tests
Documentation of all test and measuring results
Which adhesive
for which application?
Anaerobic adhesives for metal
bonding and mixed connections
DELO-ML
High exibility
–
–
+++
++
++
+
High temperature range of use
+++
++
+
++
++
++
High strength
+++
+++
++
+++
+++
+++
Tension-equalizing
–
–
+++
++
++
+
Dual-curing
–
–
5327
UB160
DB133
DB135 / DB136
DB180
DB154
anaerobic curing
anaerobic
UV-curing
with UV light
(320 – 380 nm)
green
colorless
Color
anaerobic light-curing with UV light
or visible light (320 – 450 nm)
clear-yellowish
DB136, DB180: uorescent
yellow
uorescent
Viscosity [mPas] at +23 °C
300
10,000
700
1,200
17,000
6,000
Curing time until initial strength
[min] at rt (approx. +23 °C),
2–4
2–4
3–6
2–4
3–6
2–4
–
–
25
10
10
6
70
70
55
60
60
65
33
40
28
40
40
35
anaerobic with Znph screws
Min. irradiation time [s]
DELO Standard 23
Off-torque [Nm] with Mon 46 Nm
Compression shear strength [MPa]
according to ISO 10123
Tensile shear strength [MPa]
Al/Al
11
8
12
13
13
13
DIN EN 1465, sand-blasted
St/St
16
14
14
16
14
16
n. d.
n. d.
130
30
40
4
– 60 to +200
– 60 to +180
– 40 to +120
– 60 to +180
– 60 to +180
– 60 to +180
Elongation at tear [%]
Industrial Adhesives
Germany · Windach / Munich
Phone +49 8193 9900-0
info@DELO.de
www.DELO.de
DIN EN ISO 527
Temperature range of use [°C]
02 / 15
DB = Dual Bonding
n. d. not determinable
UB = Universal Bonding
"