CFG-6mm glyceroled cut carbon fibres0 pages
APPLY.CARBON sa
contact@apply-carbon.fr
Z.A. Lanveur F-56440 LANGUIDIC tel +33 2 97 65 10 89 fax +33 2 97 65 11 20
CFG-6mm
CFG-6mm
glyceroled cut carbon fibres
TECHNICAL DATA SHEET
n°13007
FICHE TECHNIQUE
mise à jour / up dated February 2013
- CFG-6mm : mixture of all origins carbon and graphite ex-PAN fibres, obtained from spools of pure carbon fibres, cut for the
widest range of short fibres applications. Underneath added glycerol overcoating, its original sizing, which can vary, is generally
compatible with the widest range of thermoplastic and thermosetting matrixes ( polymers and elastomers ), also: rubbers, papers,
concretes, paints etc ; its compatibility needs to be checked on each new batch and for each new application.
application
- CFG-6mm : mélange de fibres de carbone et graphite ex-PAN de toutes origines, obtenu de bobines de fibres de carbone pures,
origines
coupées pour le plus large éventail d’applications fibres courtes. Sous le surensimmage glycérol, son ensimage originel, variable, est
généralement compatible avec le plus large éventail de matrices thermodurcissables et thermoplastiques ( polymères et élastomères )
mais aussi : caoutchoucs, papiers, bétons, paints etc ; sa compatibilité doit être vérifiée à chaque lot et pour toute nouvelle
application.
application.
PROPRIETES VALEURS MOYENNES ( val. Mini. ) (1)
PROPERTIES
AVERAGE VALUES ( minimum values )
Chemical and physical properties are unchanged.
Les propriétés chimiques et physiques sont celles d'origine.
Teneur en fibres de carbone *
dont fibres exPAN *
(1)
100% ( 100% )
100 (100%
0%)
100% (100%)
Carbon fibres content*
from whitch exPAN fibres*
*
* before glycerol addition
Teneur en carbone
94% ( >92% )
Carbon content
Taux d’ensimage (avant glycérol)
Surensimage glycérol
1.4 % ± 0.6
3,5% ± 0,2
Sizing level (before glycerol addition)
glycerol oversizing
Densité ( fibre continue )
1.7 < d < 2.
Density ( continuous fibre. )
∅ monofilaments
7 m ± 2
Mono filament diameter
Résistivité volumique
Ω
15 Ω m ( 20 maxi )**
*avant ajout glycérol
** : résistivité volumique moyenne
de n ( n > 1000 ) monofilaments
Volume resistivity
** : average volume resistivity of
n ( n > 1000 ) monofilaments.
Résistance en traction
Allongement à rupture
Module de Young (traction)
3.5Gpa ( 3.)
1.5% ( 1.2)
230Gpa ( 200.)
Tensile strength
Elongation at break
Young’s modulus (tensile)
Longueur moyenne
6mm ± 0,5
mean length
Distribution
95% en masse en 6mm ±0.3
95% in mass inside 6mm ±0.3
≈ 0.55kg/dm3 ±0.05
Densité apparente
Contamination métallique
(2)
Distribution
Bulk density
< 0.001g/1000g
Metal contamination
(2)
(1) except for grey marked fields,
except for grey marked fields,
average values excerpt from the technical data sheets of the ex.PAN ‘‘high strength’’ fibres that we use in
our mixture for more than 90%. The ≤10% remaining are ‘‘high modulus’’ fibres from same various producers : TORAY-SOFICAR
,TOHO-TEIJIN-TENAX, HEXCEL, CYTEC.... All these values, in the same way for length, distribution, bulk density, metal contamination,
responsibility.
are given as a rough guide and do not in any way engage APPLY.CARBON’s responsibility.
(1) sauf lignes grisées,
valeurs moyennes relevées dans les fiches techniques des producteurs des fibres ex.PAN haute résistance qui sont
utilisées dans notre mélange pour plus de 90%. Les ≤10% restants sont des ‘‘hauts modules’’ des mêmes divers producteurs: TORAYSOFICAR ,TOHO-TEIJIN-TENAX, HEXCEL, CYTEC.... Toutes ces valeurs, de même que longueur, distribution, densité apparente,
contamination métallique, sont données à titre indicatif et ne sauraient pas engager APPLY.CARBON contractuellement.
contractuellement.
.
(2) all our cut or milled fibres are purified through powerful magnets separators. Although very rare, some non magnetic metal
particles stay possible. An Xrays control permits to eliminate particles from 1mm 3 (Pb, Cu) to 6mm3 ( Al ) depending on metal density ;
aluminium chips or sheets, even of several cm2 , can’t be detected.
toutes nos fibres coupées ou broyées sont purifiées par passage dans de puissants séparateurs magnétiques. Des inclusions
(2)
de métaux amagnétiques, bien que rarissimes, restent possibles. Un contrôle par rayons X permet d’éliminer des particules à partir de
1mm3 (Pb, Cu) à 6mm3 ( Al ) selon la densité du métal ; des copeaux ou feuilles d’aluminium très minces, même de plusieurs cm 2,
sont indétectables.
Health and Safety : Carbon fibres are not dangerous for health. However, as short fibres and dusts, they cause irritation on skin, eyes,
tract ; the sizing sometimes causes allergies. People will have to wear dust protections as face masks, spectacles, light overalls,
gloves. Carbon fibres are conductive of electricity
electricity.
Santé, Sécurité : Les fibres de carbone ne sont
pas dangereuses pour la santé. Toutefois, sous forme de fibrettes courtes et de poussières, elles sont irritantes pour la peau, les
yeux, les voies respiratoires ; les produits d’ensimage peuvent parfois provoquer des allergies. On devra s’en protéger avec masques
à poussières, combinaisons légères, lunettes, gants. Les fibres de carbon sont conductrices de l’électricité.
l’électricité.