Bars - Superimphy® 90 - N070900 pages
Bar
Corrosion application
SY 90
SY 90 is an aged hardening nickel-chromium-cobalt alloy. It combines a high tensile strength up to 600° with good creepC
rupture properties up to 920° It has a good corro sion resistance in wide oxidizing environment. It presents also a good
C.
resistance to cyclic heating.
1. Chemical content
Ni
UNS N07090
2. Heat treatments
Co
Fe
Ti
Al
Base
Wr 2.4632
Cr
18-21
16-21
<2
2-3
1-2
3. Applications
Our standard is : Solution : 1080° 2 to 4 hrs, ai r
C,
cooling + Aged hardening 700° - 16hrs, air cooling
C
Other treatments are possible. Please consult us.
•
•
•
•
Elements for gas turbines (discs, blades, …)
Forgings
Ring sections
Hot working tools
4. Shapes – Tolerances – Destinations
Round bars
Section
Ø 4 to Ø 20mm
Process
Surface Conditions
Cold bars
Raw, rectified, chamfrened
Length
3 to 6m
Weight
min 400Kg
Wooden box or narrow
strapping
drawn straightened and
rectified
h9, Ra < 1,2µm
Packaging
Tolerances
Ø 100 to Ø 300mm
Hot-rolled bars
Forged bars
Peeled, rectified, polished,
Peeled, ground, rectified,
roller burnished, raw
polished, raw
3 to 6m
min 1000Kg
Wooden box or narrow
Secured package
strapping
Peeled + roller burnished
h11, Ra < 3,2µm
+/- 3mm
Peeled (Ra < 6,3µm)
< 1mm/m
+/- 3mm
-0/+ 0,8mm for diameter < 80mm
-0/+1,2mm for diameter > 81mm
Ground
Straightness
Ø 20 to Ø 140mm
- 0 / +3mm
< 4,2mm/m
< 4,2mm/m
Uses
Bars for machining
Bars for machining or hot-transformation
Customer processes used
in manufacturing finished
parts
Machining, free-cutting
Machining, forging, stamping, hot-rolling, drop forging,
ring beking, drawing, upsetting, ring rolling,…
Aperam Alloys Imphy
Innovatis
5, rue Luigi Cherubini
F- 93212 St Denis
Tel + 33 1 71 92 00
Fax + 33 1 92 07 93
nickel.alloys@aperam.com
www.aperam.com/alloys-imphy
© March 2012
__________________________________________________________
"