CeraLab0 pages
â
CeraLab
M.E.SCHUPPâ CeraLabâ
Laboratory Ceramic Crucibles & Boats
up to 1,350°C Application Temperature
®
®
M.E.SCHUPP CeraLab are high-speed analysers for
determination of carbon and sulphur contents in metals/iron
and steel, non-ferrous alloys, rubber, carbon black, cement,
slag, coal, kerosene, etc.
The product has a high thermal shock resistance and a very
low content of carbon and sulphur.
Crucibles and boats can be supplied in different dimensions
and different chemical compositions.
MATERIAL PROPERTIES
Laboratory Crucibles
white
min. 5 MPa
1,350
white
1,300
> 45 % Al2O3,
Carbon content < 0.02 %
3
2.40 g/cm
Typical Alloy
80 % SiO2, 20 % Al2O3
Density
1.8 to 2.3 g/cm
Ø 25,5 mm, H 26 mm
(stackable)
-6 -1
4 to 4.8x10 K
Standard Dimensions
Thermal Expansion Coefficient
Technical Drawing
3
L 88 mm, W 13 mm, H 8 mm
-
Photography: Lothar Wels – www.wels-images.com
Color
Bending Strength
Max. Application Temperature [°C]
Laboratory Boats
"