Panex® 35 Uni-Directional Fabrics0 pages
Technical Datasheet
Panex® 35 Uni-Directional Fabrics
Stitch-Bonded Uni-Directional Carbon Fabrics
Description
Panex® 35 Stitch-Bonded Uni-Directional Carbon
Fabrics are produced from our Panex® 35 50K
Continuous Tow Carbon Fiber. Unique fiber
spreading techniques are utilized to obtain a
wide range of UD fabric weights for a varied set of
composite part applications. Quick composite
part build-up is cost effectively achieved with our
diverse weight range of low-cost carbon fabric
products.
Material Overview
UD150
UD200
UD300
UD400
0° Carbon Panex® 35 50K
158
200
309
403
500
600
865
90° Glass 34 dtex
10
10
10
10
10
10
-
Polyester Veil
-
-
-
-
-
-
30
Polyester Stitch 76 dtex
6
6
6
6
6
6
5
Binder Resin Powder
8
8
8
-
-
8
-
Total Fabric Weight
182 g/m2
5.37 oz/yd2
224 g/m2
6.61 oz/yd2
333 g/m2
9.82 oz/yd2
419 g/m2
12.36 oz/yd2
516 g/m2
15.22 oz/yd2
624g/m2
18.40 oz/yd2
900 g/m2
26.54 oz/yd2
UD500
UD600
UD900V
Average values shown. Typical Fiber Volume Fraction (FVF) is 55%.
Standard Epoxy Resin System
Fabric Construction
UD150
UD200
UD300
UD400
UD500
UD600
UD900V
Stitch Length
3.6 mm
5.5 mm
Stitch Pattern
Tricot
½ Tricot
Cure Thickness
Roll Width
Roll Length
.21 mm
.25 mm
.37 mm
.46 mm
.57 mm
.69 mm
122 cm
30 cm - 61 cm - 122 cm
100 m
1.00 mm
50 m
30 m
Standard Epoxy Resin System
Thicknesses vary by process