Panex® 30 woven carbon fiber fabrics0 pages
Technical Datasheet
Panex® 30 Fabric (PW03, PW06, SW08)
Graphitized Spun Yarn Carbon Fabric
Description
Panex® 30 Woven Carbon Fabrics tailorability
results from controlling the yield on rovings and
yarns, and allows for a variety of finished composite thicknesses. The spun yarns have many
surface fibrils that protrude in various directions
at various lengths from the surface. This fiber loft
contributes to high cross-ply tensile and interlaminar shear strengths for 2-D composite materials. Contour conformation without wrinkling is
another advantage of spun yarn fabrics. Panex®
30 materials undergo a vacuum graphitizing
process and long temperature soak, resulting in a
very thermally stable and chemically pure fabric
with low oxidation rate.
Material Overview
Plain Weave (PW03)
SI
US
Plain Weave (PW03)
Applications
Applications of composites fabricated with
Panex® 30 Woven Fabrics include low cost
carbon-carbon materials and other processes
where chemical vapor infiltration or prepregging
is required.
Plain Weave (PW06)
SI
US
Satin Weave (SW08)
SI
US
Areal Weight
115 g/m2
3.4 oz/yd2
237 g/m2
7.0 oz/yd2
288 g/m2
8.5 oz/yd2
Count (W x F)
175 x 175
yarns/10 cm
45 x 45
yarns/in
113 x 113
yarns/10 cm
29 x 29
yarns/in
160 x 160
yarns/10 cm
38 x 38
yarns/in
Thickness
406 microns
16 mils
673 microns
20 mils
890 microns
35 mils
838 mm
33 inch
1,067 mm
42 inch
73 m
80 lyds
36 m
40 lyds
Standard Widths
Roll Length
Yarn Input
Carbon Content
Density
Oxidation Rate
2/27
838 & 1,067 mm 33 & 42 inch
36 m
2/10
99%
1.75 g/cc (0.063 lb/in3)
1% per our at 932°F (500°C)