Biresin® U14190 pages
Product Data Sheet
nnnnVersion 07/2010
nnnnBiresin® U1419
nnnnVacuum Casting resin
nnnnAreas of Applicatio
nnnnProduct Benefits
nnnnManufacture of tough-hard and flexible prototype
nnnnparts
nnnnManufacture of abrasion and impact stressed
nnnnmouldings in production facility
nnnnSimulation of soft-PVC, PE and rubber
nnnnFast curing with good flowability
nnnnTough-hard and very flexible
nnnnHigh tear strength
nnnnHigh rebound elasticity
nnnnDyeablewith Biresin®-Farbpasten
nnnnDescription
nnnnBasis
nnnnResin
nnnnHardener
nnnnTwo-component-PUR-system
nnnnBiresin®U1419, polyol, yellowish-transparent, unfilled
nnnnBiresin®U1419, MDI-based isocyanate, amber, unfilled
nnnnIndividual Components | Biresin® U1419 | Biresin® U1419 |
Viscosity, 25°C mPas | ~ 3,500 | ~ 180 |
Density g/cm3 | 1.06 | 1.23 |
Mixing ratio resin to hardener in parts by weight | 100 | 16 |
Mixed viscosity, 25°C mPas | -2,700 | |
Potlife, 500 g, RT min | 6-7 | |
Demoulding time at 70°C mould temperature min | >60 | |
Curing time, RT d | 1 -3 |
Physical Data (approx. values) | ||
Biresin® U1419 Resin with hardener | Biresin® U1419 | |
Colour | yellowish-transparent* | |
Density IS01183 g/cm3 | 1,1 | |
Shore hardness ISO 868 | A98( D54 ) | |
Tensile strength ISO 527 MPa | 25 | |
Elongation at break ISO 527 % | 375 | |
Tear strength ISO 34 N/mm | 68 | |
Linear shrinkage, test specimen: . . . n/ -in internal % 500 mm x 40 mm x 10 mm | 0.05 | |
Abrasion resistance ISO 4649 A mm3 | 90 |
* dependent on raw materials the colour can differ without different mechanical properties
nnnnPackaging
nnnnWorking packages
nnnnIndividual components
nnnnBiresin® U1419 A+B Pack
nnnnBiresin® U1419 resin
nnnnBiresin® U1419 hardener
nnnn6 x 1.0 kg net resin +
nnnn6 x 0.16 kg net hardener in a box
nnnn10 kg net
nnnn1.6 kg net
nnnnCD
nnnn>
"