Product Data Sheet
Version 07 / 2010
SikaBlock® M1000
Areas of Application
Product Benefits
Manufacture of true-to-size gauges and moulds
Manufacture of foundry models and master
models
High dimensional stability and low density
Low density for good handling
Good edge stability
Good heat distortion temperature
Easily mechanically workable
Dense, high-tensile surface
Low thermal expansion coefficient
Description
Basis
Adhesive
Filler
Polyurethane, white
Biresin ® Power Adhesive Thix, two-component-epoxy-system
Biresin ® Spachtel weiß, two-component-polyester-system, white
Physical Data (approx. values)
SikaBlock® M1000
Density
ISO 845
g/cm³
1.0
Shore hardness
ISO 868
-
Flexural strength
ISO 178
MPa
48
E-Modulus
ISO 604
MPa
1,800
Compressive strength
ISO 178
MPa
47*
Impact resistance
ISO 179 Ue kJ/m²
13
Heat distortion temperature
ISO 75 B
°C
85
Coefficient of thermal expansion (CTE), αT
DIN 53 752
K-1
D 75
55 x 10 -6
* at 10% compressive strain
Processing Data
Adhesives / Filler
Adhesive
Biresin ® Power
Mixing ratio
in parts by weight
Adhesive Thix
Filler
Biresin ® Spachtel
100 : 33
100 : 2
Potlife
min
30
5
Setting time
h
16
weiß
> 20 min
Packaging
Board materials
SikaBlock® M1000
Adhesive
Biresin® Power Adhesive Thix,
AB Pack
Biresin® Spachtel weiß, resin
Filler
BPO-Paste, hardener
1500 mm x 500 mm x 50 mm, 25 pieces / pallet
1500 mm x 500 mm x 75 mm, 16 pieces / pallet
1500 mm x 500 mm x 100 mm, 12 pieces / pallet
6 x 0.9 kg net resin +
6 x 0.3 kg net hardener in a box
2 x 9.84 kg net cartridges
6 x 1.96 kg net tins in a box
2 x 0.16 kg net sticks (for cartridges)
6 x 0.04 kg net tubes in a box (for tins)
SikaBlock® M1000 1 / 2
Tooling & Composites
Tooling board of low density
"