Biresin® CR1200 pages
Product Data Sheet
Version 06 / 2012
Biresin® CR120
Areas of Application
Product Benefits
For infusion or injection processing
Specially for applications when higher temperature resistance is required
Approved by Germanischer Lloyd for the
production of components
One resin with two hardeners with different reactivity
Uniform mixing ratio of 100 : 30
The reactivity can be adapted by mixing the
hardeners
Because of low mixed viscosity fast infiltration of
dry fabrics and nonwovens
Glass transition temperatures up to 120°C
dependent on curing conditions
Description
Basis
Resin (A)
Hardener (B)
Hardener (B)
Two-component-epoxy-system
Biresin® CR120, epoxy resin, tranlucent
Biresin® CH120-3, amine, colourless to yellowish
Biresin® CH120-6, amine, colourless to yellowish
Physical Data
Resin (A)
Individual Components
Biresin®
CR120
Hardener (B)
Biresin®
CH120-3
Biresin®
CH120-6
Viscosity, 25°C
mPas
900
< 10
35
Density, 25°C
g/ml
1.13
0.94
0.93
Mixing ratio
in parts by weight
100
30
Mixture
Potlife, 100 g / RT, approx. values
min
90
180
Mixed viscosity, 25°C, approx. values
mPas
240
250
Processing
The material and processing temperatures should be from 18 to 35°C.
Before demoulding precuring of at least 2 h at 60°C is recommended.
To clean brushes or tools immediately Sika Reinigungsmittel 5 is recommended.
Additional informations are available in “Processing Instructions for Composite Resins”.
Biresin ® CR120 1 / 4
Tooling & Composites
Composite resin system
"